X-ray microtomography of fatigue crack closure as a function of applied load in Al-Li 2090 T8E41 samples

摘要

Crack closure is held to be responsible for very low fatigue crack growth rates in many alloys such as Al-Li 2090 T8E41, and early crack face contact during unloading or prolonged contact during loading seems to reduce the driving "force" forcrack extension. High resolution x-ray computed tomography (i.e., microtomography) allows one to image the entire volumes of samples and to quantify opening as a function of applied load over the entire crack surface. Crack closure results are reportedfor a fatigue crack grown under load ratio R=0.1 in a compact tension sample of Al-Li 2090 T8E41; the crack was free to choose its path unconstrained by side-grooves which are normally used to suppress crack deflection. The inter-relationship betweencrack path, crack face contact and applied load level are discussed.