CRACK ANALYSIS IN AS CAST LARGE SIZE INGOT OF A HIGH STRENGTH STEEL

摘要

The mechanism of crack apparition of an as cast high strength low alloy steel ingot was investigated. Elemental, mechanical and crystallographic analyses proved that tensile stresses accumulated during casting and annealing are responsible of crack generation. The crack propagation is favored by the formation of chromium carbides at prior austenite grain boundaries.