An algae-elastomer composite including an elastomer matrix; algae; and a mixing additive sufficient to achieve a desired property. The algae can be present in a milled condition having a particle size value of between about 10 and 120 microns. The algae is mixed with the elastomer matrix in a dry condition having a moisture content of below about 10%. A method of preparing the algae-based elastomer composite is provided that includes the steps of: premixing an elastomer matrix; adding an algae filler; adding a mixing additive that includes a plasticizer; forming an elastomer-algae blend by blending the algae and elastomer to a temperature sufficient to be further mixed, wherein the temperature is about 10° C. higher than the temperature sufficient for the elastomer alone; adding and mixing a curing or vulcanizing agent for the elastomer dispersing the elastomer-algae blend; and heating and curing the elastomer-algae blend into a final form.