NICKEL ALLOY HAVING SUPERIOR HOT WORKABILITY AND CREEP RUPTURE CHARACTERISTIC AT HIGH TEMPERATURE
NICKEL ALLOY HAVING SUPERIOR HOT WORKABILITY AND CREEP RUPTURE CHARACTERISTIC AT HIGH TEMPERATURE
展开▼
机译:镍合金具有出色的高温加工性和高温蠕变断裂特性
展开▼
页面导航
摘要
著录项
相似文献
摘要
PURPOSE:To obtain the titled Ni alloy by adding a prescribed amount of Y or Mg to the composition of an Ni alloy called 'Inconel 718(R)'. CONSTITUTION:0.005-0.15% Y and/or 0.01-0.03% Mg is added to an Ni alloy consisting of, by weight, 50-55% Ni, 17-21% Cr, 4-6% Nb and Ta, 2-4% Mo, 0.1-1.5% Al, 0.1-2% Ti and the balance Fe. The resulting alloy has considerably improved hot workability and creep rupture characteristics at high temp. as compared with 'Inconel 718(R)'. The rupture time of the alloy is about twice as that of the 'Inconel 718(R)' and the alloy has a remarkably prolonged rupture life.