MOLDED PARTS OR PANELS FROM SILICA AEROGELS.

摘要

Shaped part based on supercritically dried silica aerogel parts in the form of spherical particles having diameters of from 0.1 to 10 mm or of sheet-like pieces having thicknesses of from 2 to 30 mm and diameters of from 1 to 5 cm, characterized in that the formed part is produced by pressing at temperatures in the range from 500 to 1000 DEG C and pressures of from 0.5 to 10 bar, under a protective gas such as nitrogen, if required, and without the addition of binders.