Automotive SLI lead-acid batteries are disclosed which are characterized by enhanced resistance to positive grid corrosion, even when exposed to the current, relatively high under-the-hood service temperatures in use with recent model automobiles. The grids are formed from either a cast lead-based alloy including from about 0.025 to 0.06% calcium, from about 0.3 to 0.7% tin and from about 0.015 to 0.045% silver, the percentages being based upon the weight of the alloy prior to casting or a wrought lead-based alloy including from about 0.02 to 0.05% calcium, from about 0.3 to 0.5% tin and 0.02 to 0.045% silver, the percentages being based upon the weight of the alloy. Aluminum in an amount of from about 0.008 to about 0.012%, based upon the as-added total weight of the alloy may be used to maintain the desired calcium content during casting. IMAGE