Method for producing polyester fiber by ultra high speed spinning method
Method for producing polyester fiber by ultra high speed spinning method
展开▼
机译:超高速纺丝法生产聚酯纤维的方法
展开▼
页面导航
摘要
著录项
相似文献
摘要
The present invention is to produce a polyester fiber by the ultra-fast spinning method with a spinning speed of 5.500m / min or more, by heating the thread yarn compressed in the spinneret by a non-contact heater that satisfies the following equation of the cylinder (linear) form To provide a method for producing a polyester fiber characterized in that it has a non-shrinkage rate (7 ~ 8%) of the gentleman level, the polyester fiber produced by the method according to the present invention is general even if manufactured by the ultra-fast spinning method Since it has a non-shrinkage rate of the stretched yarn level, the fabric density does not decrease after weaving, so it can be manufactured into a high quality fabric. Heater radius (mm) = A x single-diameter In the above formula, A is the experimental constant, the first heater; A = Experimental constant, the second heater having a range of 15-20; Experimental constant having a range of A = 40-50, single yarn diameter (0.54mm) = 75d / 36f (15μ) x number of filaments (36).
展开▼
机译:本发明是通过用满足以下的式子的非接触加热器加热喷丝头中压缩的丝线,通过超快纺丝法,以5500m / min以上的纺丝速度来制造聚酯纤维的。为了提供一种生产聚酯纤维的方法,其特征在于其具有绅士水平的非收缩率(7〜8%),根据本发明的方法生产的聚酯纤维通常是均匀的。如果通过超快速纺丝方法制造,由于它的拉伸丝水平没有收缩率,因此编织后织物密度不会降低,因此可以制造出高质量的织物。加热器半径(mm)= A x单直径在上式中,A是实验常数,第一个加热器; A =实验常数,第二加热器的范围为15-20;实验常数的范围为A = 40-50,单纱直径(0.54mm)= 75d / 36f(15μ)x细丝数量(36)。
展开▼