In a method for producing a magnetic recording medium, at least one magnetic layer is formed on a nonmagnetic support by coating. After all coating processes are completed, heat treatment is performed by heat-treating the support, which is undergone all the coating processes, at 95 to 140° C. for 1.0 to 10.0 seconds with continuously applying tension of from 1.0 to 4.0 kg/m to the support. Then, calendering process is performed at a temperature lower than the temperature of the heat treatment.
展开▼
机译：在制造磁记录介质的方法中，通过涂覆在非磁性载体上形成至少一个磁性层。在完成所有涂覆过程之后，通过在95至140℃下对经历了所有涂覆过程的载体进行热处理来进行热处理。持续1.0到10.0秒，并向支撑物连续施加1.0到4.0 kg / m的张力。然后，在低于热处理温度的温度下进行压延处理。