PROBLEM TO BE SOLVED: To provide a manufacturing method capable of manufacturing a high strength cement hardened body in which the construction work in placing is easily and rapidly carried out and the explosion fracture of the high strength cement hardened body caused by heat in fire is improved (prevented from the explosion fracture) in the high strength cement hardened body having a compressive strength exceeding 105 MPa.;SOLUTION: The explosion resistant high strength cement hardened body is manufactured by kneading, forming and setting a compound containing 100 pts.mass cement particle having 2,500-5,000 cm2/g Blaine specific surface area, 10-40 pts.mass fine particle having 5-25 cm2/g BET specific surface area, 10-50 pts.mass inorganic particle A having 5,000-30,000 cm2/g Blaine specific surface area, 5-35 pts.mass inorganic particle B having 2,500-5,000 cm2/g Blaine specific surface area, a water reducing agent, water and organic fibers each having different length.;COPYRIGHT: (C)2004,JPO
展开▼
机译:解决的问题:提供一种能够制造高强度水泥硬化体的制造方法,该方法能够容易且迅速地进行放置中的施工作业,并且改善了由火热引起的高强度水泥硬化体的爆炸破坏。 (防止爆炸破裂)在抗压强度超过105 MPa的高强度水泥硬化体中;解决方案:防爆高强度水泥硬化体是通过捏合,成型和凝固包含100 pts.mass水泥颗粒的混合物来制造的具有2,500-5,000 cm 2 Sup> / g布莱恩比表面积,10-40 pts的具有5-25 cm 2 Sup> / g BET比表面积的细颗粒,10- 50点具有5,000-30,000 cm 2 Sup> / g布莱恩比表面积的无机颗粒A,5-35点具有2500-5,000 cm 2 Sup> /的无机颗粒B g布莱恩比表面积,减水剂,水和有机纤维长度各不相同。;版权:(C)2004,日本特许厅
展开▼