ANATASE TYPE TITANIUM OXIDE FINE PARTICLES AND METHOD FOR PRODUCING ANATASE TYPE TITANIUM OXIDE FINE PARTICLES
ANATASE TYPE TITANIUM OXIDE FINE PARTICLES AND METHOD FOR PRODUCING ANATASE TYPE TITANIUM OXIDE FINE PARTICLES
展开▼
机译:锐钛型氧化钛细颗粒及其制备方法
展开▼
页面导航
摘要
著录项
相似文献
摘要
PROBLEM TO BE SOLVED: To provide anatase type titanium oxide fine particles having high freedom with respect to the range of absorbable lights and a method for producing the anatase type titanium oxide fine particles.;SOLUTION: The anatase type titanium oxide fine particles have a band gap Eg of 3.87 eV≤Eg≤4.13 eV and are generated by pulse laser ablation with a pulsed laser beam having a laser fluence of 0.25 J/cm2 or more to a raw material consisting of rutile type titanium oxide and being placed in a liquid such as distilled water, ammonia aqueous solution, nitric acid aqueous solution and the like.;COPYRIGHT: (C)2009,JPO&INPIT
展开▼
机译:解决的问题:提供相对于可吸收光的范围具有高自由度的锐钛矿型氧化钛微粒和制备该锐钛矿型氧化钛微粒的方法。间隙Eg为3.87eV·Eg·4.13eV,并且是通过脉冲激光烧蚀而产生的,该脉冲激光束的激光通量为0.25J / cm 2 Sup>以上,由金红石型钛构成氧化物,并置于蒸馏水,氨水溶液,硝酸水溶液等液体中;版权所有:(C)2009,JPO&INPIT
展开▼