COMPOSITION CONTAINING OXIDES OF ZIRCONIUM, CERIUM AND ANOTHER RARE EARTH HAVING REDUCED MAXIMAL REDUCIBILITY TEMPERATURE, AND METHOD FOR PREPARING AND USING SAME IN THE FIELD OF CATALYSIS

摘要

The invention relates to a composition containing oxides of zirconium, cerium and another rare earth different from cerium, having a cerium oxide content not exceeding 50 wt% and, after calcination at 1000°C for 6 hours, a maximal reducibility temperature not exceeding 500°C and a specific surface of at least 45 m²/g. The composition is prepared according to a method that comprises continuously reacting a mixture containing compounds of zirconium, cerium and another rare earth having a basic compound for a residence time not exceeding 100 milliseconds, wherein the precipitate is heated and contacted with a surfactant before calcination.