PROBLEM TO BE SOLVED: To provide silicon oxycarbide ceramic excellent in discharge capacity and cycle property and exhibiting high input characteristic when used as an anode active material for a nonaqueous electrolyte secondary battery.SOLUTION: There is provide porous silicon oxycarbide ceramic having a tap density of 1.10 g/cmto 1.50 g/cmwhen 1000 times tapping is conducted in the case of an average particle diameter Dof 5 to 30 m and a total pore volume at a relative pressure of a nitrogen adsorption isothermal curve of 0.986 of 0.03 to 0.500 cm/g.
展开▼
机译:要解决的问题:提供一种放电容量和循环性能优异并且在用作非水电解质二次电池的负极活性物质时具有高输入特性的碳氧化硅陶瓷。解决方案:提供一种振实密度为1的多孔碳氧化硅陶瓷。当平均粒径Dof为5至30 m且氮气吸附等温曲线的相对压力为0.986时的总孔体积为0.03至0.500 cm / g时,进行1000次攻丝时,1.10 g / cm至1.50 g / cm 。