CHEMICALLY DURABLE ALUMINOSILICATE GLASS COMPOSITIONS AND GLASS ARTICLES FORMED THEREFROM
CHEMICALLY DURABLE ALUMINOSILICATE GLASS COMPOSITIONS AND GLASS ARTICLES FORMED THEREFROM
展开▼
机译：化学耐用的铝硅酸盐玻璃成分和以其制成的玻璃制品
展开▼
页面导航
摘要
著录项
相似文献
摘要
In embodiments, a glass composition may include: greater than or equal to 71 mol. % and less than or equal to 83 mol. % SiO2; greater than or equal to 1 mol. % and less than or equal to 11 mol. % Al2O3; greater than or equal to 5 mol. % and less than or equal to 18 mol. % alkali oxide, the alkali oxide comprising greater than 3 mol. % Li2O and at least one of Na2O and K2O; greater than or equal to 1 mol. % and less than or equal to 8 mol. % alkaline earth oxide, the alkaline earth oxide comprising MgO and at least one of CaO, BaO, and SrO; and at least one of TiO2, ZrO2, HfO2, La2O3 and Y2O3, wherein TiO2+ZrO2+HfO2+La2O3+Y2O3 is greater than 0 mol. % and less than or equal to 6 mol. % and Al2O3+TiO2+ZrO2+HfO2+La2O3+Y2O3 is greater than or equal to 2 mol. % and less than or equal to 12 mol. %.
展开▼
机译：在实施方案中，玻璃组合物可包含：大于或等于71摩尔。 ％并且小于或等于83mol。 ％SiO 2 ;大于或等于1 mol。 ％并且小于或等于11摩尔。 ％Al 2 O 3 ;大于或等于5 mol。 ％并且小于或等于18mol。 ％的碱金属氧化物，该碱金属氧化物包含大于3mol。 ％Li 2 O和Na 2 O和K 2 O中的至少一个;大于或等于1 mol。 ％并且小于或等于8mol。 ％的碱土金属氧化物，该碱土金属氧化物包含MgO和CaO，BaO和SrO中的至少一种。 TiO 2 ，ZrO 2 ，HfO 2 ，La 2 O 3 < / Sub>和Y 2 O 3 ，其中TiO 2 + ZrO 2 + HfO 2 < / Sub> + La 2 O 3 + Y 2 O 3 大于0摩尔。 ％并且小于或等于6摩尔。 ％和Al 2 O 3 + TiO 2 + ZrO 2 + HfO 2 + La 2 O 3 + Y 2 O 3 大于或等于2摩尔。 ％并且小于或等于12摩尔。 ％。
展开▼