首页> 外国专利> Production method of environment-friendly water-repellent synthetic leather using non-fluorine water repellent agent

Production method of environment-friendly water-repellent synthetic leather using non-fluorine water repellent agent

机译:使用无氟憎水剂的环保型憎水合成革的生产方法

摘要

The present invention relates to a method of manufacturing an eco-friendly water-repellent synthetic leather using a non-fluorine water repellent, and includes a water-dispersible polyurethane and a non-fluorine water repellent in a polyester tricot brushed fabric to maximize water repellency while being eco-friendly and harmless to the human body. The impregnation step of impregnating the water-repellent mixture for impregnation, the mangle step of adjusting the moisture content to 40-80% by compressing the fabric impregnated with the impregnating water-repellent mixture, the water-dispersible polyurethane and non-fluorine water repellent on the fabric that has undergone the mangle step A silver layer forming step of coating a water-repellent mixture for coating containing, a drying step of hot air drying the fabric subjected to the silver layer forming step at 90° C. to 110° C. for 2 to 4 minutes through a dryer, and 140° C. It includes a curing step of curing in a curing machine for 4 to 6 minutes at ~150 ℃.
机译:本发明涉及一种使用非氟防水剂的环保型疏水性合成皮革的制造方法,其包括在聚酯经编织物拉丝织物中包含水分散性聚氨酯和非氟防水剂以最大程度地提高疏水性。既环保又对人体无害。浸渍用于浸渍的憎水混合物的浸渍步骤,通过压缩浸渍有浸渍憎水混合物的织物,水分散性聚氨酯和非氟憎水剂来将水分调节至40-80%的mangle步骤在已经进行了上浆步骤的织物上涂覆银层形成步骤,该步骤包括涂覆用于涂覆的疏水混合物,该干燥步骤包括将在90℃至110℃下进行了银层形成步骤的织物进行热风干燥的干燥步骤。通过干燥机在140℃下干燥2至4分钟。该固化步骤包括在固化机中在约150℃下固化4至6分钟的固化步骤。

著录项

相似文献

  • 专利
  • 外文文献
  • 中文文献
获取专利

客服邮箱:kefu@zhangqiaokeyan.com

京公网安备:11010802029741号 ICP备案号:京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有
  • 客服微信

  • 服务号