首页> 外文OA文献 >Flexural strength of fibre reinforced concrete under elevated temperature
【2h】

Flexural strength of fibre reinforced concrete under elevated temperature

机译:高温下纤维增强混凝土的抗弯强度

代理获取
本网站仅为用户提供外文OA文献查询和代理获取服务,本网站没有原文。下单后我们将采用程序或人工为您竭诚获取高质量的原文,但由于OA文献来源多样且变更频繁,仍可能出现获取不到、文献不完整或与标题不符等情况,如果获取不到我们将提供退款服务。请知悉。

摘要

The study observes and examines the effects of elevated temperature on the fibre reinforced concrete’s ability to withstand flexure loading. The fibres used are steel, synthetic and kenaf fibre. Addition of fibres into reinforced concrete may increase the ductility and cracking resistance. To explore the effects of elevated temperature, a furnace was used to heat the prepared specimens to 400°C, 600°C and 800°C. Steel fibre reinforced concrete was found to maintain some amount of flexure capacity even at 800°C, due to the high melting point, 1300°C, of the steel fibres. However, not all properties of concrete may improve with the addition of fibres. High temperature that may be due to structure usage or accidents is a concern that has to be considered when choosing the right material for reinforcing the concrete matrix. By understanding the effects of elevated temperature on the various types of fibre reinforced concrete, a better choice of fibres can be made for different structural usage.
机译:该研究观察并检验了高温对纤维增强混凝土承受挠曲载荷的能力的影响。使用的纤维是钢,合成纤维和洋麻纤维。将纤维添加到钢筋混凝土中可以增加延展性和抗裂性。为了探索高温的影响,使用了一个炉子将准备好的样品加热到400°C,600°C和800°C。由于钢纤维的高熔点(1300°C),发现钢纤维增强混凝土即使在800°C时也能保持一定的挠曲能力。但是,并非所有的混凝土性能都可以通过添加纤维来改善。选择合适的材料来增强混凝土基体时,必须考虑由于结构使用或事故引起的高温。通过了解高温对各种类型的纤维增强混凝土的影响,可以针对不同的结构用途更好地选择纤维。

著录项

  • 作者

    Cheong Lip Sing;

  • 作者单位
  • 年度 2015
  • 总页数
  • 原文格式 PDF
  • 正文语种 en
  • 中图分类

相似文献

  • 外文文献
  • 中文文献
  • 专利

客服邮箱:kefu@zhangqiaokeyan.com

京公网安备:11010802029741号 ICP备案号:京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有
  • 客服微信

  • 服务号