Some load limits and self-lubricating properties of plain spherical bearings with molded graphite fiber reinforced polyimide liners to 320 C

摘要

Plain spherical bearings with molded liners of self-lubricating graphite fiber-polyimide composite were developed and their dynamic load capacities were determined. Liners were prepared by transfer molding a prepolymer resin-fiber mix into the space between the ball and outer race, the completing polymerization under heat and pressure. Bearing dynamic load capacities were in excess of 140 MPa (20,000 psi) from room temperature to 260 C and about 70 MPa (10,000 psi) at 320 C. Friction coefficients were about 0.20 at room temperatures and light loads and tended to decrease with increasing temperatures and loads to about 0.15. Thermal expansion of the liner at uniform bearing temperatures of 200 C or higher produced a bearing preload which could be alleviated by providing an initial internal diametral clearance of 0.05 to 0.10 mm.