Effect of substrate chemical pretreatment on the tribological properties of graphite films

摘要

Rubbed films of natural flake Madagascar graphite were applied to ASTM A-355(D) steel with chemical surface pretreatments of zinc phosphate, gas nitride, salt nitride, sulfo-nitride, and with mechanical pretreatment (sandblasting). SAE 1045 steel pins were slid against these films using a pin-on-disk tribometer. The results indicate that two different lubricating mechanisms can occur. In the chemical surface pretreatment, the graphite can mix together to form a surface layer of the two constituents and this plasticity flowing layer provides the lubrication. The longest endurance lives and the lowest pin wear rates were obtained with this mechanism. In the other, surface topography appeared to control the mechanism. A rough surface was necessary to serve as a reservoir to supply the graphite to the flat metallic plateaus where it was sheared in very thin films between the plateaus and the sliding pin surface. For this mechanism, chemical pretreatment seemed to do little more than serve as a means for roughening the surface. Mean friction was not significantly influenced by chemical pretreatment, but surface roughness effects were observed.