Opacification of high temperature fibrous insulation

摘要

A study was conducted to determine the merits of adding particulate materials to silica fiber felts to increase their resistance to the passage of thermal radiation. Laboratory samples containing 5, 10, and 15 percent of chromium oxide, silicon carbide, and titanium dioxide were prepared and evaluated in accordance with ASTM C-518 thermal conductivity test method at 425 C (800 F) mean temperature. The titania particles averaging 3-4 micrometers in diameter were found to be the most effective. This was followed by a short plant run, in order to confirm the initial results on the laboratory samples. These samples were tested according to ASTM C-201 High Temperature Calorimeter from 93 C to 760 C (200 F to 1400 F) mean temperature. The ten percent by weight of titania resulted in an optimum effectiveness, and reduced the conductivity over 20 at 760 C (1400 F).