Effects of External Environments on the Short Beam Shear Strength of Filament Wound Graphite/Epoxy

摘要

Filament wound graphite/epoxy samples were immersed in seawater, deionized water, and toluene at room temperature and 80 deg C for 5, 15, and 43 days, and in methanol at room temperature for 15 and 43 days. The percent weight gains and short beam shear strengths were determined after environmental exposure. Samples immersed in deionized water and seawater had higher percent weight gains than those immersed in toluene at room temperature and 80 deg C. The percent weight gains for samples immersed in methanol at room temperature were comparable to those of deionized water and seawater immersed samples. A comparison of percent decreases in short beam shear strengths could not be made due to a large scatter in data. This may indicate defects in samples due to machining or variations in material properties due to processing.