Calorimetric Determination of the Enthalpy of Formation and a Description of the Defect Structure of the Ordered beta-Phase (Ni,Cu)(1-x)Al(x)

摘要

In order to describe thermodynamically the defect structure of an ordered B-Hume-Rothery phase, the heat of formation of (Ni,Cu)(1-x)Al(x) was measured at 1100 K as a function of concentration in the range x (sub Al) = 0.4 and 0.55 for three substitution rations x (sub Ni)/x (sub Cu) = infinity; 11; 5. The heat of formation of the NiAl beta-phase is strongly negative. For the stoichiometric composition it is -72.2 kJ/g-atom. On both the nickel-rich side and the aluminum-rich side the magnitude of the enthalpy of formation decreases linearly with concentration. Substitution of nickel for copper decreases the magnitude of the enthalpy of formation over the entire homogeneity range for the phase (Ni,Cu)(1-x)Al(x). The curve for the enthalpy of formation as well as the literature values for the chemical potential of aluminum are described with great accuracy by the disorder model of Wagner-Schottky.