Hybrid aerogel rigid ceramic fiber insulation and method of producing same

摘要

A hybrid insulation material comprises of porous ceramic substrate material impregnated with nanoporous material and method of making the same is the topic of this invention. The porous substrate material has bulk density ranging from 6 to 20 lb/ft.sup.3 and is composed of about 60 to 80 wt silica (SiO.sub.2) 20 to 40 wt alumina (Al.sub.2 O.sub.3) fibers, and with about 0.1 to 1.0 wt boron-containing constituent as the sintering agent. The nanoporous material has density ranging from 1.0 to 10 lb/ft.sup.3 and is either fully or partially impregnated into the substrate to block the pores, resulting in substantial reduction in conduction via radiation and convention. The nanoporous material used to impregnate the fiber substrate is preferably formed from a precursor of alkoxysilane, alcohol, water, and an acid or base catalyst for silica aerogels, and from a precursor of aluminum alkoxide, alcohol, water, and an acid or base catalyst for alumina aerogels.