Effect of ion-beam induced strain on the nucleation density of chemical vapour deposited diamond

摘要

The effect of ion implantation on the nucleation of CVD diamond on silicon and diamond substrates has been investigated. The strategy employed is to create laterally confined regions of strain in the substrates by focused MeV implantation of light ions. Raman Microscopy has been employed to obtain spatially resolved maps of the strain in these implanted regions. On diamond substrates a homo-epitaxial CVD diamond film was grown on top of both the implanted and unimplanted regions of the substrate. Raman analysis of the film grown on top of the implanted region revealed it to be under slightly tensile strain as compared to that grown on the unimplanted diamond substrate. The film deposited on the implanted portion of the diamond showed a lower fluorescence background; indicating a lower concentration of incorporated defects. These results suggest that the strain and defects in the diamond substrate material have an important influence on the quality of the homo-epitaxially grown diamond films. 6 refs., 5 figs. (Atomindex citation 26:069422)