Phase Formation During Corrosion Experiments with Two Simulated Borosilicate Nuclear Waste Glasses

摘要

Corrosion products resulting from the reaction of simulated high-level radioactive waste glasses with various solutions have been identified. At 200degC, in saturated NaCl, a degree of reaction of 10 g C31-3 glass or 2.6 g SON 68 glass per liter of solution was obtained. Analcime, vermiculite (a phyllosilicate) and a 2:1 zinc silicate are the major silica containing alteration products for the C31-3 glass. Analcime was the only silicate alteration product which could be identified for SON 68 glass. C31-3 glass appeared to be less reactive with a quinary brine containing Mg/sup ++/ than with NaCl. With the quinary brine, montmorillonite (a phyllosilicate) was the predominant silica containing alteration product. Hydrotalcite (a Mg-Al hydroxysulfate) and montmorillonite were the major Al-containing phases. A phyllosilicate, probably montmorillonite, was observed to form during the reaction of SON 68 glass with quinary brine. With either glass, modified NaCl brines which contained small amounts of MgCl/sub 2/ seem to have the effect of decreasing the amount of analcime and increasing the amount of phyllosilicate which is formed. In the case of C31-3 glass, there is approximately enough Mg, Al and Zn to precipitate most of the leached Si; measured Si concentrations remain well below that expected for amorphous silica. SON 68 glass has less Zn, Al and Mg than C31-3 glass and much higher Si concentrations of the leachates. (ERA citation 13:005501)