Influence of Aluminum on the Formation Behavior of Zn-AI-Fe Intermetallic Particles in a Zinc Bath

摘要

The shape, size, and composition of dross particles as a function of aluminum content at a fixed temperature were investigated for aluminum added to the premelted Zn-Fe melt simulating the hot-dip galvanizing bath by a sampling methodology. In the early stage, less than 30 minutes after Al addition, local supersaturation and depletion of the aluminum concentration occurred simultaneously in the bath, resulting in the nucleation and growth of both Fe_2Al_5Zn_x and FeZn_(13). However, the aluminum was homogenized continuously as the reaction proceeded, and fine and stable FeZn_(10)Al_X formed after 30 minutes. An Al-depleted zone (ADZ) mechanism was newly proposed for the "η - > η + ξ - > δ phase transformations. The ξ phase bottom dross partly survived for a relatively long period, i.e., 2 hours in this work, whereas the η phase disappeared after 30 minutes. In the early stage of dross formation, both Al-free large particles as well as high-Al tiny particles were formed. The dross particle size decreased slightly with increased reaction time before reaching a plateau. The opposite tendency was observed when the Al content was 0.130 mass pct; with a relatively high Al content, the nucleation of tiny η phase dross was significantly enhanced because of the high degree of supersaturation. This unstable η phase dissolved continuously and underwent simple transformation to the stable δ phase. The relationship between nucleation potential and supersaturation ratio of species is discussed based on the thermodynamics of classical nucleation theory.