Alumina- and titania-based monolithic catalysts for low temperature selective catalytic reduction of nitrogen oxides

摘要

The selective catalytic reduction of NO±N02 (NOr) at low temperature (180—2300C) with ammonia has been investigated with copper-nickel and vanadium oxides supported on titania and alumina monoliths. The influence of the operating tem-perature, as well as NH3/NO~ and NO/NO2 inlet ratios has been studied. High NO~ conversions were obtained at operating conditions similar to those used in industrial scale units with all the catalysts. Reaction temperature, ammonia and nitrogen dioxide inlet concentration increased the N20 formation with the copper-nickel catalysts. while no increase was observed with the vanadium catalysts. The vanadium-titania catalyst exhibited the highest DeNQ activity, with no detectable ammonia slip and a low N20 formation when NH3/NOA inlet ratio was kept below 0.8. TPR results of this catalyst with NO/NH3/02. N02/NH3/02 and NO/N02/NH3/02 feed mixtures indicated that the presence of NO~ as the only nitrogen oxide increases the quantity of adsorbed species, which seem to be responsible for NiG formation. When NO was also present, N2O formation was not observed.