Highly Textured FeCo Thin Films Deposited by Low Temperature Pulsed Laser Deposition

摘要

The effect of the deposition temperature (Tdep) on the crystallographic orientation of pulsed laser-deposited FeCo/MgO(100) thin film was determined by means of X-ray reflectivity and high resolution trasmission electron microscopy analysis and was correlated with the magnetic anisotropy properties measured by angle dependent hysteresis loops. Highly textured films with a bcc structure and very smooth surface were obtained even at room temperature, the film being [100] and [110] oriented, at T-dep = 25 degrees C and 150 degrees C, respectively. The cubic symmetry is reflected in the angular dependence of remanent magnetization, showing a 4-fold character, whose in-plane distribution is consistent with the different crystallographic orientations of the films. The high structural quality, even at room temperature, is reflected in a high value of the saturation magnetization and low coercivity, matching the requirements for technological applications.