Abstract The ternary aurides La4In3Au10 and Yb4In3Au10 and the platinide U4In3Pt10 with ordered Zr7Ni10 type structure were synthesized from the elements by induction-melting in sealed tantalum tubes or via arc-melting. The polycrystalline samples were characterized by powder X-ray diffraction and the structures were refined from single crystal X-ray diffractometer data: Cmce, a = 1426.7(3), b = 1020.3(2), c = 1025.2(2) pm, wR2 = 0.0441, 1510 F2 values, 46 variables for La4In3Au10, a = 1361.5(3), b = 998.3(2), c = 1007.8(2), wR2 = 0.0804, 1404 F2 values, 46 variables for Yb4In3Au10 and a = 1344.4(3), b = 973.9(2), c = 978.9(2), wR2 = 0.0922, 741 F2 values, 48 variables for U4.15In3.03Pt9.82 (with small degrees of In/U, respectively Pt/In mixing on Wyckoff sites 4a and 8 f). The La4In3Au10, Yb4In3Au10 and U4In3Pt10 structures contain pronounced two-dimensional gold, respectively platinum substructures which are filled and condensed by two crystallographically independent indium and rare earth atoms. The crystal chemical features clearly classify these intermetallics as aurides and platinides. The physical properties of U4In3Pt10 were characterized by means of magnetic and electrical transport measurements. The compound exhibits metallic conductivity and shows no magnetic ordering down to 1.72K. Its magnetic behavior is governed by hybridization between 5f and ligand electrons that results in significant delocalization of the 5f states. Graphical abstract Ternary aurides La4In3Au10 and Yb4In3Au10 and platinide U4In3Pt10 with ordered Zr7Ni10 type structure.