Reversible four-color electrochromism triggered by the electrochemical multi-step redox of Cr-based metallo-supramolecular polymers

摘要

Four color electrochromism (yellow, magenta, blue, and navy) has been achieved in Cr(iii)-based metallo-supramolecular polymers (polyCr), which were synthesized by 1 : 1 complexation of Cr ions and 1,4-di[[2,2 ':6 ',2 ''-terpyridin]-4 '-yl]benzene (L). The polymer structure was determined by X-ray absorption fine structure (XAFS) measurement and X-ray photoelectron spectroscopy (XPS). The molecular weight of polyCr was calculated as 3.2 x 10(7) Da using right angle light scattering (RALS). The EXAFS fitting indicated that the bond distances of Cr-N are 2.020 angstrom and 2.208 angstrom. A film of polyCr shows multi-color electrochromism (EC) or absorption: a sharp peak at 380 nm at 0 V vs. Ag/Ag+ (yellow), a sharp peak at 510 nm and a broad peak at 800 nm at -0.6 V vs. Ag/Ag+ (magenta), a broad peak at 610 nm and between 700-900 nm at -1.2 V vs. Ag/Ag+ (blue), a broad peak between 450-900 nm at -1.8 V vs. Ag/Ag+ (navy). The transmittances change (Delta T), the switching times for coloring and bleaching (T-c, T-b) and the coloration efficiency (eta(c), eta(b)): [Delta T, (T-c, T-b), (eta(c), eta(b))] were [39.2%, (5.56 s, 1.39 s), (169 cm(2) C-1, 230 cm(2) C-1)] at 510 nm between -0.6 and 0.2 V vs. Ag/Ag+, [67.0%, (6.93 s, 2.52 s), (138 cm(2) C-1, 172 cm(2) C-1)] at 610 nm between -1.2 and 0.2 V vs. Ag/Ag+, [86.1%, (6.80 s, 3.03 s), (167 cm(2) C-1, 134 cm(2) C-1)] at 780 nm between -1.8 and 0.2 V vs. Ag/Ag+, respectively, during the cycles. The durability experiment indicates that polyCr shows an EC property for at least 100 cycles.