Impact of antimony trioxide on the physico-mechanical and flammability properties of irradiated recycled rubber powder and waste polyethylene composites

摘要

The physicomechanical behavior and flammability properties of waste polyethylene and recycled waste rubber powder blend (WPE/RWRP/MA) filled with antimony trioxide (Sb _2O _3), at different contents 5, 10, 15, and 20 wt %, and irradiated with different gamma radiation doses, namely 50, 75, 100, and 150 kGy, were investigated by thermogravimetric analysis (TGA), differential scanning calorimetry (DSC) and limiting oxygen index (LOI) measurements. Tensile strength, elongation at break, elastic modulus, hardness, swelling properties, and electric conductivity behaviors were also investigated. Experimental results emphasized that Sb _2O _3 particles retard degradation and flammability of the composite. The LOI increases from 16 to 20.9 with 20 wt % Sb _2O _3 specimen irradiated with 150 kGy. Improvement in thermal stability at conditions of 15 wt % Sb _2O _3 and a dose of 75 kGy was demonstrated by TGA.DSC measurements showed that T _m significantly increased in the presence of the filler. Mechanical characterization tests showed a significant increase in tensile strength within the range 5-10 wt % Sb _2O _3.