Impact strength improvement of wood flour-recycled polypropylene composites

摘要

In this research, the improvement of the impact strength of wood flour-recycled polypropylene (PP) composites through impact modification was studied. For this purpose, a virgin polypropylene (VPP) was thermomechanically degraded by five extrusions under controlled conditions in a twin-screw extruder at a rotor speed of 100 rpm and a temperature of 190°C. PP (VPP and recycled PP at the second and fifth stages) and wood flour were compounded at 50 wt % wood flour loading in a counterrotating twin-screw extruder in the presence different contents of ethylene vinyl acetate (EVA) to produce the wood flour-PP composites. From the results, the composites containing recycled PP exhibited significantly lower impact strengths. The addition of EVA up to 9 wt % increased the impact strengths of the composites made with PP recycled two and five times by about 63 and 41%, respectively. The composites containing VPP exhibited higher impact strengths than those containing recycled PP and EVA.