Structural studies of annealed neodymia-silica composite synthesized by solgel technique

摘要

Nd2O3-SiO2 binary oxide was prepared by solgel technique using tetra-ethoxysilane and neodymium nitrate as precursor materials and HCl as a catalyst. The prepared samples were subjected to heat treatment in the temperature range from 600 to 1100 degrees C for different time duration. Characterization of heat treated samples was carried out by using X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR) and scanning electron microscopy (SEM). The effect of sintering temperature and time on structural changes of Nd-doped silica has been discussed. The sample sintered at 1100 degrees C for 12 h shows the formation of monoclinic Nd2O3 nanocrystallites in silica matrix with average grain size similar to 18 nm.