Phase Morphology and Mechanical Properties of Polyamide-6/Polyolefin Elastomer-g-Maleic Anhydride Blends

摘要

The effects of addition of varying amounts of polyolefin elastomers (POE) (with and/or without grafted maleic anhydride) on the morphology and mechanical properties of polyamide-6 (PA6)-based blends were studied. Scanning electron microscopy (SEM) was employed to obtain some detailed quantitative analyses of the morphology of the fracture behavior for the blends containing 80 wt% PA6 and 20 wt% total elastomer. Impact strength, tensile strength, and flexural strength were also measured for these blends. The results showed that POE and PA6 were an incompatible system, but the POE-g-MAH was compatible and had a toughening effect on PA6. PA6-g-POE was formed through the reaction between POE-g-MAH and PA6 during the melt extrusion process, which reduced the size of the dispersed phase and improved the impact and tensile strength of the blends. The impact strength was improved by nine times compared with the pure PA6 or the binary blend PA6/POE when the blend ratio of the ternary blend PA6/POE/POE-g-MAH was 80/16/4.