Failure Analysis of a Titanium Strut Tank Support in the Space Shuttle Columbia

摘要

A titanium midtank strut support from the Columbia space shuttle Was submitted for failure analysis. Stereomicroscopy, light optical microscopy, and scanning electron microscopy with energy-dispersive spectroscopy were used to investigate the failed part. Evidence of melting was found on the fracture surface. Additionally, the high temperature associated with the melting was combined with cooling from the β-phase field, as indicated by the formation of a martensitic microstrucure in the surrounding material. Craters were found on the surface of the part due to impact of foreign particles containing iron, nickel, and chromium. Failure of the titanium strut support was due to the severe high tem-peratures encountered as a result of the shuttle breakup and re-entry into the earth's atmosphere.