Effect of additives on mechanical properties of oxidation-resistant carbon/carbon composite fabricated by rapid CVD method

摘要

The optimum composition of additives was obtained by the orthogonal design test method for oxidation-resistant carbon/carbon composites (C/C) fabricated by the rapid CVD method. The effect of additives on mechanical properties was examined. The additives used in this test included silicon carbide, silicon nitride, and metla borides. Additives doped into the matrix of C/C increase not only the initial oxidation temperature from 400 to 657deg C (64%), but also its flexural strength from 121 to 254 MPa (110%), and flexural modulus from 25 to 45 GPa (96%). The increase of mechanical properties is considered to be due to the formation of a metallic carbon-boron compound in the microstructure.