Penetration of Liquid Steel in Sand Molds, Part II: Chemical Reactions at the Mold/Metal Interface During Casting of Steel

摘要

Steel castings were made in sand molds with various binders and coatings to study the effect of mold atmosphere on chemical penetration. The atmosphere at the mold-metal interface and the extent of chemical penetration depended strongly on the carbon and moisture content of the mold. Chemical penetration occurred on most castings but was usually prevented with mold coatings. Experiments shoed that steel can suffer chemical penetration after solidification but it is easily removed. A combined heat and mass transfer model for the steel and mold was developed. It correctly predicted the atmosphere for a green sand mold without seacoal addition and the occurrence of chemical penetration early in the casting and later after solidification.