Effect of coating bath composition on the properties of electroless nickel-boron films

摘要

The effect of borohydride, thallium acetate, ethylenediamine and sodium hydroxide concentrations, and the coating bath temperature on both the coating rate and boron content of the electroless Ni - B films was investigated systematically. The Ni - B coating rate increased with the increase in thallium acetate and sodium hydroxide concentrations, but it was not very sensitive to the borohydride concentration. Below 90 g L-1 ethylenediamine concentration the coating efficiency was significantly low and above this value as the ethylenediamine concentration increased the coating rate decreased slightly. Below 85 degrees C the coating rate was very low and above this temperature it was insensitive to the bath temperature. The boron content of Ni - B film increased with the increase in the borohydride concentration and the bath temperature, and decreased with the increase in thallium acetate and ethylenediamine concentrations. Up to 50 g L-1 sodium hydroxide concentration, the boron content of the film increased and above this concentration it was insensitive to the sodium hydroxide concentration. As the boron content of Ni - B film increased, both the corrosion resistance and microhardness of Ni - B film increased. Heat treatment brought significant improvement in the microhardness but the corrosion resistance of Ni - B film was observed to decrease due to the disappearance of the amorphous characteristics of the as-deposited Ni - B film and the formation of the Ni - B compound phases. (c) 2007 Elsevier B.V. All rights reserved.