The Effect of Electron Beam (EB) Irradiation in Presence of TMPTA on Cure Characteristics and Mechanical Properties of Styrene Butadiene Rubber/Recycled Acrylonitrile-Butadiene Rubber (SBR/NBRr) Blends

摘要

The effect of electron beam (EB) irradiation on the cure characteristics and mechanical properties of unirradiated and irradiated SBR/NBRr blends were investigated. The SBR/NBRr blends were prepared at 95/5, 85/15, 75/25, 65/35, and 50/50 blend ratio with and without the presence of a polyfunctional monomer, trimethylolpropane triacrylate (TMPTA). Results indicated that the scorch time t₂, cure time t₉₀ and minimum torque (M_L) of irradiated SBR/NBRr blend decreased, but the maximum torque (M_H) particularly at 35 and 50Â phr of NBRr (recycled NBR) increased with the presence of TMPTA. The stress at 100% elongation (M100), hardness, cross-linking density and tensile strength (particularly after 15Â phr of NBRr content) of irradiated SBR/NBRr blends increased after irradiation but the elongation at break (EB) and resilience decreased. The irradiated SBR/NBRr blends showed lower thermal stability than non-irradiated blends. Scanning electron microscopy proved the enhancement in tensile strength when more NBRr were added in SBR matrix where the irradiated surfaces demonstrate more irregularity with increasing crack branching (fracture planes are located at different heights) due to the increased of cross-linked density.