Effect of crosslinker feed content on catalaytic activity of silver nanoparticles fabricated in multiresponsive microgels

摘要

We investigated the effect of crosslinking density of poly(N-isopropyl acrylamide-co-acrylic acid) micro-gels on catalytic activity of silver nanoparticles fabricated hybrid microgels. Multiresponsive poly(N-isopropyl acrylamide-co-acrylic acid) microgels with 2, 4, 6 and 8 mole percentage of N,N-methylene-bis-acrylamide were synthesized by emulsion polymerization. These microgels were characterized by dynamic light scattering and were used as mi-croreactors to synthesize silver nanoparticles. Hybrid system was characterized by ultraviolet-visible spectroscopy. The catalytic activity of hybrid microgels with different crosslinker content was compared by studying the reduction of p-nitrophenol as a model reaction. Kinetics of reaction was monitored by spectrophotometry. The value of the apparent rate constant decreases from 0.568 to 0.313 min~(-1), when content of crosslinker are increased from 2 to 8 mole percentage respectively. This decreases in value of apparent rate constant is due to increase in diffusional barrier offered by high crosslinking of polymer network at high mole percentages of N,N-methylene-bis-acrylamide.