Influence of silica aerogel on the properties of polyethylene oxide-based nanocomposite polymer electrolytes for lithium battery

摘要

In this study, a series of nanocomposite polymer electrolytes (NCPEs) with high conductivity and lithium ion transference number, PEO/LiClO_4/SAP, were prepared from high molecular weight polyethylene oxide (PEO), LiCIO_4 and low content of homemade silica aerogel powder (SAP), which had higher surface area and pore volume than the conventional silica particle. From the SEM images it was found that the SAP nanopar-ticles were well dispersed in the PEO polymer electrolyte matrix. The characterization and interactions in the CPEs were studied by DSC, XRD, FT-1R and~7 Li NMR analysis. The ac impedance results showed that the ionic conductivity of the CPE was significantly improved by the addition of the as-prepared SAP. The maximum ambient ionic conductivity obtained from the CPE with EO/Li = 6 and 2 wt.% of SAP (06A2) was about threefold higher than that of the corresponding polymer electrolyte without SAP (06). In addition, the lithium ion transference number (t~+) of 06A2 at 70℃ was as high as 0.67, which was also three times higher than that of 06 and has not been previously reported for the PEO-LiX-based polymer electrolytes.