Influence of rapid thermal annealing on the process of aluminum induced crystallization of amorphous Si

摘要

The effects of annealing methods on the crystallization process and microstructure of polycrystalline silicon (poly-Si) films obtained by aluminum-induced crystallization (AIC) of amorphous Si (a-Si) films were comparatively investigated. Glass/Al/a-Si structures were annealed by rapid thermal annealing (RTA) and conventional furnace at 500 ℃ for different times in Ar. As compared to furnace annealing, AIC of a-Si films annealed by RTA possesses a shorter period of nucleation time, a higher nucleation density and reduces the process time to form continuous poly-Si films. It is revealed that the continuous Si films obtained by both RTA and conventional furnace annealing are polycrystalline in nature, exhibiting good microstructures with Raman peaks at 518 cm~(-1) and full-width at half-maximums of 6.43-6.48 cm~(-1).