Structural And Magnetic Properties Of La_(0.72)(ca_(1-x)sr_x)_(0.28) Mno_3 (x = 0 To 1) Manganites

摘要

Polycrystalline manganites within the compositional variation La_(0.72)(Ca_(1-x)Sr_x)_(0.28)MnO_3 (x = 0, 0.25, 0.50, 0.75, 1.0) were synthesized by solid-state reaction method. An initial orthorhombic structure was observed at x = 0, with a subsequent change to rhombohedral structure for x ≥ 0.25. The Curie temperature of the compounds exhibited a marked dependence with the Sr content, with general variations between 190 K (x = 0) and 364 K (x = 1.0), while the saturation magnetization at room temperature showed a small variation between the range 0.30 and 0.38 T. The magnetocaloric effect, measured through heat capacity experiments, showed a maximum entropy variation of -2.56 J/kg · K at x = 0.25, besides a maximum adiabatic temperature variation of 1.13 K. Results are interpreted in terms of the structural transition observed and its effect on the radius of the A-site of the perovskite structure.