Impact of different surface treatments and repair material reinforcement on the flexural strength of repaired PMMA denture base material

摘要

This study assessed the impact of surface treatments and repair resin reinforcement with zirconium oxide nano-particles (nano-ZrO_(2)) on flexural strength (FS) of repaired denture base. A total of 320 heat-polymerized acrylic resin specimens were prepared and sectioned creating 2-mm gap. According to repair surface treatment, specimens were distributed into four groups: I) methyl methacrylate (M); II) alumina-blasted (AB); III) AB+silane coupling agent (SC); and IV) AB+methacrylate based composite bonding agent (MA). Groups were subdivided into 4 (n =20) according to nano-ZrO_(2) concentration (0, 2.5, 5, 7.5 wt%). Half the specimens were thermo-cycled before testing. FS was determined by three-point bending test. Statistical analysis was done using ANOVA and Tukey-Kramer multiple comparison tests, with α =0.05. Alumina-blasting+(SC) or (MA) significantly increased FS of repaired specimens compared to control (p <0.05). All surface-treated specimens combined with nano-ZrO_(2) reinforced repair resin significantly increased FS.