Effects of different surface treatments on bond strength of an indirect composite to bovine dentin

摘要

Background: Several surface treatments could be used to improve the bond strength (BS) between indirect composites and cement. Aim: To evaluate the BS of an indirect composite submitted to different surface treatments, cemented to bovine dentin. Settings and Design: One hundred and fifty conical cavities were prepared in slices of bovine dentin and bulk filled with the composite. Materials and Methods: After curing and removal from the cavity, the restorations were treated according to the groups (n = 10): C-untreated, S-Sandblasting; SS-Sandblasting + silane; F-hydrofluoric acid; FS-hydrofluoric acid + silane; SF-Sandblasting + hydrofluoric acid; SFS-Sandblasting + hydrofluoric acid + silane; E-ethanol; ES-ethanol + silane; SE-Sandblasting + ethanol; SES-Sandblasting + ethanol + silane; P-H₂O₂; PS-H₂O₂ + silane; SP-Sandblasting + H₂O₂; SPS-Sandblasting + H₂O₂ + silane. After cementation, push-out test was performed in a universal testing machine. Statistical Analysis: Data were submitted to nonparametric tests (Kruskal–Wallis and Mann–Whitney U-tests, α = 0.05). The failure mode was observed under a stereomicroscope and the topography by scanning electronic microscopy (SEM). Results: Sandblasted groups led to the highest BS values, (P P Pgroups showed the lowest BS values. The number of cohesive or mixed failures was related to higher BS values. SEM evaluation showed major irregularities only for sandblasted groups. Conclusions: Sandblasting was a safe surface treatment for the indirect composite, increasing the BS values. Hydrofluoric acid applied after sandblasting damaged the BS values and should not be recommended while ethanol and H₂O₂, when applied after sandblasting, were effective in increasing BS values.