A Structural Study of Epoxidized Natural Rubber (ENR-50) and Its Cyclic Dithiocarbonate Derivative Using NMR Spectroscopy Techniques

摘要

A structural study of epoxidized natural rubber (ENR-50) and its cyclic dithiocarbonate derivative was carried out using NMR spectroscopy techniques. The overlapping 1H-NMR signals of ENR-50 at δ 1.56, 1.68–1.70, 2.06, 2.15–2.17 ppm were successfully assigned. In this work, the 13C-NMR chemical shift assignments of ENR-50 were consistent to the previously reported work. A cyclic dithiocarbonate derivative of ENR-50 was synthesized from the reaction of purified ENR-50 with carbon disulfide (CS₂), in the presence of 4-dimethylaminopyridine (DMAP) as catalyst at reflux temperature. The cyclic dithiocarbonate formation involved the epoxide ring opening of the ENR-50. This was followed by insertion of the C–S moiety of CS₂ at the oxygen attached to the quaternary carbon and methine carbon of epoxidized isoprene unit, respectively. The bands due to the C=S and C–O were clearly observed in the FTIR spectrum while the 1H-NMR spectrum of the derivative revealed the peak attributed to the methylene protons had split. The 13C-NMR spectrum of the derivative further indicates two new carbon peaks arising from the >C=S and quaternary carbon of cyclic dithiocarbonate. All other 1H- and 13C-NMR chemical shifts of the derivative remain unchanged with respect to the ENR-50.