Hydroxyapatite Coating on Alloys CoCrMo-TiN with Sol-Gel Method

摘要

Hydroxyapatite is synthesized by precipitation-sonification using calcium from field snail shell and powder phosphorus from (NH 4 ) 2 HPO 4. The calcium value was measured by atomic absorption spectrophotometer was 82.82%.The temperatures were varied on 600, 800, and 1000 o C to determine the best temperature of the coating. The best temperature was used to superimpose the HAp on the CoCrMo-TiN metal alloy using the modified sol-gel method. The layer on the metal alloy was identified with x-ray diffraction (XRD) and corrosion test. The XRD result showed that most of the CoCrMo-TiN metal alloy surface was coated by HAp. Beside HAp, there were several other phases such as calcium phosphate, carbonate apatite type A and type B. The best result of the corrosion test was showed in CoCrMo-TiN metal alloy coated with HAp with the smallest corrosion rate 0.0082 mpy.