Synthesis and characterization of silver molybdate nanowires, nanorods and multipods

摘要

Silver molybdate nanowires, nanorods and multipods like structures have been prepared by an organic free hydrothermal process using ammonium molybdate and silver nitrate solutions. The powder X-ray diffraction (PXRD) patterns reveal that the silver molybdate belongs to anorthic structure. The thickness, 200a€“500 nm, for silver molybdate nanorods/wires and 2a€“5 e???m for microrods are identified from SEM images. UV-visible spectrum of silver molybdate nanorodsanowires shows maximum absorbance at 408 nm. Photoluminescence (PL) spectrum exhibits UV emission at 335 nm, violet emission at 408 nm and a weak green emission at 540 nm. The influence of hydrothermal synthesis conditions on silver molybdate nanowires, nanorods and multipods compositions were established.