Degradation and passivation of CulnSe_2

摘要

The degradation of CuInSe_2 absorbers in ambient air is observed by the decay of the quasi-Fermi level splitting under well defined illumination with time. The decay is faster and stronger in absorbers with [Cu]/[In] < 1 than in ones with a higher ratio. It can be attributed to the oxidation of the sample. Epitaxial films containing no Na show very similar trends, indicating that decay and oxidation are independent of the Na content. A standard CdS layer commonly used as buffer in solar cells, terminates the decay even over many months. Aged absorbers can be completely restored by a KCN etch.