Change in Concentration of Amorphous Region Due to Crystallization in PTT/PET Miscible Blends

摘要

In a miscible crystalline/crystalline blend of poly(trimethylene terephthalate) (PTT) and poly(ethylene terephthalate) (PET), the PET spherulites grew at 240 °C when the PTT content was 30 wt% or less. The growth rate of PET spherulites decreased with time due to the exclusion of PTT from the growth front of PET spherulites into the amorphous region, resulting in a three-stage crystallization process. Due to the exclusion, the spherulite growth stopped before the volume filling of the PET spherulites, causing the formation of an excluded PTT amorphous region. When the temperature was lowered from 240 °C to 210 °C, the PTT spherulites grew in the excluded PTT amorphous region. The spherulite growth rate of PTT in the excluded PTT amorphous region was equivalent to that of a blend of 60–70 wt% PTT in 30/70 PTT/PET. These results suggest a significant change in the PTT concentration in the amorphous region, from the initial PTT content of 30 wt% to 60–70 wt%, due to the exclusion of PTT during the melt crystallization of PET at 240 °C.