An investigation on electrochemical behavior of Mg-5%Pb alloy, Mg-6%Al alloy and Mg-6%Al-5%Pb alloy(mass fraction) in 3.5% Na Cl(mass fraction) solution was conducted using electrochemical measurements and corroded morphology observation, in which solid solution and the as-aged state of each alloy were compared to discuss the influence mechanism of lead and aluminium on the electrochemical properties of alloys. The X-ray diffraction(XRD) analysis was performed to make microstructure characterization. The electrochemical results indicate that the corrosion of Mg-5%Pb alloy is predominated by homogeneous pitting and dissolution of PbCl_2 film due to Cl ions attack, while corrosion crevice propagates along grain boundaries in solid solution of Mg-6%Al alloy and the micro galvanic corrosion also plays vital role in Mg_(17)Al_(12) phase containing experimental alloys. The co-existence of lead and aluminium in magnesium alloy increases corrosion current density and electrochemical activity as well. The comparison between solid solution and the as-aged state demonstrates that Mg_2 Pb and Mg_(17)Al_(12) somewhat increase corrosion resistance but lighten anodic polarization by facilitating corrosion product flaking off.
展开▼