Morphological stability of Ni(Al)Ni_3Al nanolaminate composites

摘要

This manuscript discusses the morphological instability observed when multilayered samples with alternating layers of gamma -Ni(Al)/ gamma '-Ni_3Al are exposed to 800C for approximately 100 hours. Samples with 20nm/20nm or 120nm/120nm layer thickness and <001> or <111> crystal orientation to the interface normal were tested. Pinching off of layers is strongly affected by crystal orientation and layer thickness. Corresponding modeling suggests that the stability of this system is sensitive to fluctuations in the volume fraction of the two phases, the aspect ratio of columnar grains in the layers, and whether coherent or semi-coherent interfaces are present.